Abstract
ABSTRACT6061-T6 sheets with 0.8 mm thickness were successfully welded using high-speed friction stir welding (FSW) technology. The microstructural evolution and fracture behaviour of the joints were studied. The results show that sound joints could be obtained at the investigated high rotational speed of 8000 rev min−1 and welding speeds of 300–1200 mm min−1. Compared with conventional rotational speed, the grain size in the nugget zone (NZ) is obviously refined under high rotational speed. The Mg2Si, Al8Fe2Si and Al2CuMg precipitates reprecipitated adequately in the NZ during high-speed FSW, resulting in the number of the precipitates increased significantly, and further alleviating the weld softening. The difference in weld softening leads to different fracture characteristics during the tensile process. After artificial aging, the maximum welding softening in all joints is located in the heat affected zone, and the fracture is characterised by brittle fracture.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.