Abstract
Ce-doped strontium bismuth titanate (SrBi4Ti4O15, SBT) powders were prepared by glycine-nitrate process at 400-500?C and the ceramics were sintered at 980?C. The phase composition, morphology and electric properties were investigated. It was found that the calcined powders consist of a single phase SBT and the calcination temperature is lower than that for the conventional solid state method. The morphology of Cedoped SBT is flake-like and the layer size decreases with Ce-addition from 12 to 2?m confirming that the addition of Ce3+ inhibits grain growth. The Curie temperature of Ce-doped SBT increased for about 20?C compared to the pure SBT. The tan ? was ~0.005 at 35?C and even below 0.05 up to 400?C. The temperature coefficient of dielectric constant was ~0.012 and the rate of frequency change was 0.01-0.04, which indicated the high stability of dielectric properties of the Ce-doped SBT. Impedance analysis revealed that the conduction mechanism of the Ce-doped SrBi4Ti4O15 ceramics is mainly grain conduction.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call