Abstract
This research is devoted to the microstructure evolution and deformation behavior of the Al-1.2Mg-0.7Si-1.0Cu-0.1Sc-0.2Zr alloy during the isothermal multidirectional forging (MDF) in a large cumulative strain and temperature range. The structure investigation of the studied alloy revealed several phases precipitated during solidification, among which θ(Al2Cu), Q(Al5Cu2Mg8Si6), Mg2Si, Sc-bearing W(AlScCu) and V(AlSi2Sc2) phases were observed. The MDF at 150–350 °C and a maximum cumulative strain of 14.4 significantly refined grain structure providing a mean grain size of 1.2–2.1 µm. The L12 structured Al3(Sc,Zr) dispersoids with a mean size of 10 ± 1 nm were formed during two-step homogenization annealing. Due to Zener pinning of the nanoscale dispersoids and fine-grained structure, the alloy exhibited near-superplastic behavior in a temperature range of 460–500 °C and strain rate range of 2 × 10−3–1 × 10−2 s−1 with the maximum elongation to failure of ~300%. After a strengthening heat treatment, the forged alloy exhibited the yield strength of 326 ± 5 MPa, ultimate tensile strength of 366 ± 5 MPa, and elongation of 10 ± 3%. The hot deformation behavior was described using the Arrhenius type model. The developed model demonstrated high predictability accuracy with a maximum average absolute relative error of 6.6%.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call