Abstract
This paper describes the microstructure evolution in a creep aged Al-Cu-Mn alloy using optical microscopy (OM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Results show the sub-grains formation and accelerated coarsening of θ′ precipitates in creep aged samples. It is observed that at an applied stress of 50MPa, as the creep temperature increases the average length of θ′ precipitates increases and their aspect ratio first increases then decreases. It is also found that after 100h of creep exposure at 200°C/50MPa, θ′ precipitates have grown to an average length of 279nm; at 225°C/50MPa to an average length of 425nm and at 250°C/50MPa they have grown to an average length of 844nm. Coarsening/growth rate of the precipitates is described by Lifshitz-Slyozov-Wagner (LSW) model.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.