Abstract
For preparing fine-grained 0.94Na0.5Bi0.5TiO3-0.06BaTiO3 lead-free ferroelectric ceramics, the precursor powders were synthesized via sol-gel method and calcined at various temperatures. The precursor powders calcined at 520 °C, 550 °C, and 600 °C exhibit mean grain sizes of 30 ± 4 nm, 54 ± 3 nm, and 78 ± 5 nm, respectively. By optimizing the synthesis parameters, the fine-grained ceramics with high relative densities (>97%) and mean grain size around 100 nm were prepared. The ferroelectric, dielectric, and piezoelectric behavior were investigated. The ceramics prepared using the different precursor powders show different piezoelectric, ferroelectric, and dielectric behavior. The ceramic calcined at 550 °C and sintered at 900 °C exhibits the breakdown strength higher than 85 kV/cm, which exhibits the maximum polarization of 38.4 ± 0.3 μC/cm2, remanent polarization of 20.6 ± 0.4 μC/cm2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.