Abstract
The microstructure and crystallographic features of a semi-austenitic precipitation hardening steel PH 15-7Mo during solution treatment, roddrawing and aging were investigated by means of optical microscope, X-ray diffraction analyzer and transmission electron microscope. It was found that the microstructure of the steel was consist of dominant austenite, small amount of martensite and 10–15 vol.% δ-ferrite after solution treatment at 1050 °C followed by cooling in water at room temperature. The austenite transformed into lath martensite during tensile roddrawing about 60% deforming companied with some coherent fine β-NiAl particles precipitated within martensite. With higher aging temperature and longer holding time, tiny carbide M23C6 particles precipitated from martensite, which kept the cubic–cubic orientation relationship (OR) with austenite and G-T OR with martensite which is different with all the reported orientations. The OR between tiny carbide M23C6 particles G-T OR with martensite was discussed in terms of crystallography of phase transformations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.