Microstructure, chemical states, and mechanical properties of V–C–Co coatings prepared by non-reactive magnetron sputtering

Abstract

V–C–Co coatings have been prepared by non-reactive magnetron co-sputtering from VC and Co targets. The microstructure, chemical states, and mechanical properties are examined as a function of Co content in the coatings. The coatings are dense, with columnar growth structures. High resolution transmission electron microscopy (HRTEM) studies identify a nanocomposite microstructure for the 12.4at.% Co coating, in which ligament-like Co-rich regions partially separate the nanocrystalline VC grains. X-ray photoelectron spectroscopy studies reveal a noticeable charge transfer from Co 2p states to C 1s states. This charge transfer, in addition to the ligament-like Co-rich regions as revealed by HRTEM, points to the formation of a strong Co/VC interface. The nanoindentation hardness of the coatings drops steadily with the Co content, from 29GPa for pure VC to ~21GPa for the 12.4at.% Co coating. Meanwhile, the plasticity characteristic increased from 0.42 to 0.53.