Abstract
A series of mesoporous TiO 2 films on borosilicate glass with ultrafine anatase nanocrystallites were successfully synthesized using a non-acidic sol gel preparation route, which involves the use of nonionic surfactant Tween 20 as template through a self assembly pathway. The microstructure of these TiO 2 films was characterized by XRD, SEM, HR-TEM, UV–Vis spectroscopy, and N 2 adsorption–desorption isotherm analysis. Their photocatalytic activities were investigated by using creatinine as a model organic contaminate in water. It was found that all mesoporous TiO 2 films prepared with Tween 20 exhibited a partially ordered mesoporous structure. The photocatalytic activity of the TiO 2 films could be remarkably improved by increasing Tween 20 loading in the sol at the range of 50% (v/v), which yielded large amount of catalyst (anatase) on the glass support and enhanced specific surface area. The optimum Tween 20 loading was 50% (v/v) in the sol, above which good adhesion between TiO 2 films and borosilicate glass could not be maintained. The final TiO 2 film (Tween 20: final sol = 50%,v/v) exhibits high BET surface area (∼ 120 m 2/g) and pore volume (0.1554 cm 3/g), ultrafine anatase nanocrystallinity (7 nm), uniform and crack free surface morphology, and improved photocatalytic activity.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.