Abstract
To enhance the wear resistance of mechanical components, laser cladding has been applied to deposit in situ VC–Cr7C3 ceramic coating on steel substrate using a pre-placed powder consisting of vanadium, carbon and high-carbon ferrochrome. The laser cladding samples were subjected to various microstructure examinations, microhardness and wear tests. The results showed that defect-free coating with metallurgical joint to the steel substrate was obtained. The quantity of VC–Cr7C3 particles gradually increased from the bottom to the top of the coating. The VC particles in nanometer were observed within the coating. Average hardness of the coating up to 1050HV was significantly higher than that of the substrate 150HV. Wear tests indicated the wear resistance of the clad coating was 4times that of the steel substrate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.