Abstract
In this work, porous TiO2 coating was fabricated on the surface of commercially pure titanium using the micro-arc oxidation (MAO) technique, and the effect of SiC particles incorporation on the microstructure and tribological properties of MAO TiO2 coating was investigated. Results show that submicron SiC particles dispersed in the MAO electrolyte were incorporated into the TiO2 coating during the MAO process and the fabricated TiO2/SiC composite coating mainly consisted of rutile, anatase and SiC phases. The pore size and surface roughness of TiO2/SiC composite coating decreased with the increasing addition amount of SiC particles in the electrolyte. Furthermore, the incorporation of SiC particles in the TiO2 coating suppressed the initiation and propagation of micro-cracks. The tribological test of coatings against GCr15 stainless steel balls show that the incorporation of submicron SiC particles in the MAO TiO2 coating decreased the friction coefficient and wear rate.
 DOI: http://dx.doi.org/10.5755/j01.ms.25.3.20089
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.