Abstract
An Fe-6.2wt%Si as-cast strip with equiaxed grains and obvious {001} fiber texture was produced by twin-roll strip casting process. The as-cast strip was successively performed by hot rolling, warm rolling and annealing. The microstructure and texture evolution at each process stage were investigated by using electron backscatter diffraction and x-ray diffraction. It was found that the finally annealed sheet was characterized by large grain size, mild γ-fiber texture and obvious {001} fiber texture. Therefore, a high magnetic induction and a low core loss were obtained in the sheet.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.