Abstract
Microstructure and tensile properties of as-cast and T6-treated Al-4%Cu-3%Si alloy with different applied solidification pressures were investigated. The pressure has significant effect on the formed microstructure. It is observed that as the pressures increase, the porosities were removed, and the size and the secondary dendrite arm spacing of primary α-Al grains decreased evidently, and the morphology of eutectic Si particles changed from long acicular to small granular type. Hence, the tensile properties of the alloy were improved. The research has shown that the aspect ratio (A.R.) of the Si particles decreased after the solution and aging treatment. The A.R of the Si particles in the alloys with applied solidification pressure decreased more remarkably and this indicated that the Si particles can be more prone to be dissolved into α-Al matrix. Thus, the increase of the elongation was achieved.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.