Abstract
This study demonstrates that simply by rolling at ambient temperature, FCC type high entropy alloy Al0.5CoCrCuFeNi can be refined to have nanocrystalline structure and exhibits outstanding combination of strength and ductility. The yield strength and ultimate tensile strength are 1284 and 1344 MPa, respectively, in combination with an elongation of 7.6%. After a short annealing at 900°C for 10 min, the elongation is doubled to 15.3% with a trade-off around 20% in strength. This excellent combination of strength and ductility is attributable to the activation of quasi-dynamic recrystallisation during cold work and the limited grain growth during 900°C annealing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.