Abstract
A nickel–titanium (NiTi)-based intermetallic coating was in-situ synthesized on a Ti–6Al–4V (TC4) substrate via laser melting deposition (LMD) using Ni–20Cr and TC4 powders. Scanning electron microscopy, X-ray diffraction, a digital microhardness tester and an electrochemical analyzer were used to evaluate the microstructure, Vicker’s microhardness and electrochemical corrosion resistance of the intermetallic coating. Results indicate that the microstructure of the intermetallic coating is composed of NiTi2, NiTi and Ni3Ti. The measured microhardness achieved is as high as ~850 HV0.2, ~2.5 times larger than that of the TC4 alloy, which can be attributed to the solid solution strengthening of Al and Cr, dispersion strengthening of the intermetallic compounds, and grain refinement strengthening from the rapid cooling of LMD. During the electrochemical corrosion of 3.5% NaCl solution, a large amount of Ti ions were released from the intermetallic coating surface and reacted with Cl− ions to form [TiCl6]2 with an increase in corrosion voltage. In further hydrolysis reactions, TiO2 formation occurred when the ratio of [TiCl6]2− reached a critical value. The in-situ synthesized intermetallic coating can achieve a superior corrosion resistance compared to that of the TC4 alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.