Abstract
The microstructure and properties of liquid-phase sintered tungsten heavy alloys were studied. The structure and segregation of the impurity elements at the interfacial boundaries were examined using scanning electron microscopy (SEM) and fine-probe energy dispersive spectroscopy (EDS) microanalysis. Test results of mechanical properties are presented and correlated with fracture behavior of the liquid-phase sintered tungsten alloys. It was found that the Fe-Ni-W alloy exhibits superior properties as compared with the Cu-Ni-W alloy. The detection of copper was found across tungsten grains and matrix that could be associated with inferior properties of the Cu-Ni-W alloy as compared to the Fe-Ni-W alloy. Although the fracture was predominantly brittle in both alloys, complex fracture modes seem to be operative due to the composite microstructure of the alloys. Evidence of microsegregation was observed that also contributed primarily to the brittle failure in the alloys. The impurity elements, such as sulfur and phosphorus, were detected at the tungsten matrix and tungsten-tungsten particle boundaries.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.