Abstract
Zirconium carbide (ZrC) ceramics have a high melting point, low neutron absorption cross section, and excellent resistance to the impact of fission products and are considered to be one of the best candidate materials for fourth-generation nuclear energy systems. ZrC ceramics with a high relative density of 99.1% were successfully prepared via pressureless sintering using a small amount of MoSi2 as an additive. The influence of the MoSi2 content on the densification behavior, microstructure, mechanical properties, and thermal properties of ZrC ceramics was systematically investigated. The results show that the densification of ZrC was significantly enhanced by the introduction of MoSi2 due to the formation of a liquid phase during sintering. In addition, the ZrC grains were refined due to the pinning effect of the generated silicon carbide. The flexural strength and Vickers hardness of ZrC ceramics with 2.5 vol% MoSi2 sintered at 1850 °C were 408 ± 12 MPa and 17.1 GPa, respectively, which were approximately 30% and 10% higher compared to the samples without the addition of MoSi2. The improved mechanical properties were mainly attributed to the high relative density (99.1%) and refined microstructure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.