Abstract
Abstract This study investigates the influence of modification on the microstructure and properties of Mn–Si–Cr alloy steel. The results indicate that the as-cast microstructure of Mn–Si–Cr alloy steel is composed of black acicular bainitic ferrite lath and white retained austenite. The microstructure of the alloy steel changes to martensite, austenite, and carbide after quenching and partitioning treatment. After rare-earth magnesium modification and compound modification, the as-cast microstructure of Mn–Si–Cr steel becomes more refined and displays a more regular arrangement. Furthermore, the martensite and austenite grains in the modified samples show refinement, and the arrangement of martensite is more systematic. Additionally, the amount of austenite decreases, and the amount of carbides increases after quenching and partitioning heat treatment. In comparison with the unmodified samples, the modified samples show negligible changes in hardness. However, the impact toughness of modified quenched and partitioned steel increases by 20 %. Moreover, the wear resistance of compound modified quenched and partitioned steel is 38 % higher than that of the unmodified sample. The compound modified sample steel exhibits excellent wear resistance and comprehensive mechanical properties.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.