Abstract
Nonmagnetic metal-matrix composite (MMC) coatings were fabricated by laser cladding with direct injection of WC-FeNiCr powder onto the N1310 nonmagnetic steel matrix. Laser cladding was conducted using a Trumpf6000 CO2 laser. The WC-FeNiCr MMCs coating was characterized using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The phase constitution in the laser cladding was identified by x-ray diffraction (XRD). No pores or macro-cracks have been found at the interface indicating good metallurgical bonding between the coating and the N1310 nonmagnetic steel matrix. Magnetic measurements were carried out with vibrating sample magnetometer (VSM) at room temperature. The MMC coating was nonmagnetic and with a relative permeability of 1.004. The XRD analysis confirmed the presence of an austenitic γ-(Fe, Ni), Cr0.19Fe0.7Ni0.11, Fe3W3C, WC and W2C phases in the laser clad layer.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.