Abstract
In this study, pure Al and Al-Al2O3 composite coatings with a low porosity and high density were prepared on magnesium alloys by cold spraying. The surface morphology, component, hardness, interfacial bonding, wear and corrosion properties were investigated. Additionally, the relationship between the interface structure and the protective coatings’ quality was preliminarily established. Pure Al powder was used to create a coating with a homogeneous and dense microstructure. The hard-phase Al2O3 in the composite coatings was non-oxidized and would reduce the porosity of the coatings to improve their density and interfacial bonding by up to 55.82 MPa. The bonding mode of the pure Al coatings is primarily mechanical, whereas the bonding mode of the Al-Al2O3 mixed coatings is mechanical and metallurgical. The tough Al2O3 particles combined to form a layer of work-hardening reinforcement that resisted wear and effectively prevented it from spreading. The three Al-based coatings had excellent corrosion properties, as evidenced by their corrosion current being several orders of magnitude lower than that of the magnesium alloy substrates. The thick coating was significantly more corrosion-resistant than the thin coating and provided greater protection to the substrate. This study offers theoretical and technological assistance for the surface protection of magnesium alloy equipment in demanding conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.