Abstract
Yttria-stabilized ZrO 2/Al 2O 3 (abridged as YSZ/Al 2O 3) nanocomposite ceramics were prepared by pressureless sintering of the green sheets of the YSZ/Al 2O 3 nanopowders synthesized by co-precipitation method. The relative density, average grain size, and phase microstructure of the YSZ/Al 2O 3 nanoceramics as a function of YSZ contents were investigated. The relative densities of the YSZ/Al 2O 3 nanoceramics are over 95% as the YSZ contents of the YSZ/Al 2O 3 nanopowders are within 20–85 mol %. The average grain sizes of the ZrO 2 and Al 2O 3 of the as-sintered YSZ/Al 2O 3 nanoceramics decrease with increasing YSZ content of the co-precipitated YSZ/Al 2O 3 nanopowders, while the content of monoclinic ZrO 2 of YSZ/Al 2O 3 nanoceramics increases with increasing YSZ content. The presence of the second phase effectively limits a rapid grain growth of the matrix alumina. The YSZ/Al 2O 3 nanoceramics with an average grain sizes below 80 nm, relative density over 95%, and hardness as high as 19.8 GPa were obtained by the pressureless sintering.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.