Microstructure and mechanical properties of WE43 magnesium alloy fabricated by direct-chill casting

Abstract

High quality WE43 magnesium alloy ingots with diameter of 500mm are successfully fabricated by direct-chill (DC) casting. The alloying elements distributed almost homogeneously across the large ingot. With the average grain size decreasing from the center to the edge of the ingot, the mechanical properties are improved gradually. After solution treatment at 525°C for 8h, the Mg14Nd2Y phases distributing along the grain boundaries are well dissolved into matrix. The direct-chill (DC) casting ingot exhibits remarkable age-hardening response from 85Hv to 117Hv after T6 treatment at 250°C. The T6 peak-aged sample exhibits ultimate tensile strength of 274MPa, yield strength of 215MPa and elongation to failure of 3.4%, which are higher than those of sand-cast and permanent mold cast WE43 alloys. The large amount of nano prismatic β′ and β1 phases precipitated during T6 treatment contribute to improved strength of the WE43 alloy.