Abstract
Three kinds of (Ti, M)(C1−x, Nx) (M = Ta, Nb, W) quaternary solid-solution powders with various nitrogen contents were synthesized by carbothermal reduction–nitridation (CRN) process. Effect of nitrogen content on the microstructure and mechanical properties of WC–(Ti, M)(C1−x, Nx)–Co cemented carbides fabricated by sinter-hot isostatic pressing (HIP) were systematically investigated in this paper. The results show that the nitrogen content in the carbonitride raw powders strongly influences the morphology, the grain size and the compositions of the cemented carbides. All the cemented carbides with different nitrogen contents have a similar microstructural appearance: weak core–rim structure consisting of solid-solution phase embedded in WC–Co system. It is also observed that the carbonitride solid solution could somewhat reduce the WC grain growth, and the effectiveness of refining and the rim thickness are sensitively related to the nitrogen content of (Ti, M)(C1−x, Nx) solid solutions. In addition, with an increase in the nitrogen content, mechanical properties of these hard metals are enhanced, which were discussed in terms of the constituent, the microstructure and the solution behavior of the carbonitride solid solutions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.