Abstract
ABSTRACT Recent studies indicated that precipitation-hardened high-entropy alloys (HEAs) possess outstanding properties. It is difficult to obtain substantial precipitated particles for HEAs at the as-cast condition. In this paper, cast precipitation-hardened high-entropy superalloys (HESAs) Ni48−x Co18Cr10.5Fe9.3Al9.7Ti4.5Mo x (at.-%, x = 1, 2, 3) were designed and prepared. All HESAs possess a high-entropy matrix and a fine γ′ particles structure. HESAs have higher ultimate tensile strength and elongation at room temperature than conventional Ni-based superalloys and close yield strength. All HESAs possess high compressive strength at elevated temperature. At 850 °C, the strengths of all alloys are higher than 800 MPa. Solid solution strengthening and precipitation strengthening were discussed. Precipitation strengthening has the greatest contribution to yield strength.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.