Abstract
AbstractIn this work, stacked SiC fibers paper‐reinforced SiC ceramic matrix composites (SiCnf/SiC CMCs) were prepared by nanoimpregnation and transient eutectic (NITE) process using ultra‐long single‐crystal SiC nanofibers. The effect of the SiCnf surface modification via boron nitride (BN) interphase deposition as well as the sintering additive (Al2O3–Y2O3) content on the density, microstructure, and mechanical properties of SiCnf/SiC CMCs has been investigated systematically. The results revealed that the laminated SiCnf/SiC CMCs feature a significant saw‐tooth‐like curve on the load–displacement test, which indicates that the obtained laminated structure with the weak interlayer binding owning to the BN coating treatment possesses significant toughening to the SiC ceramics. Specifically, the SiCnf/SiC CMCs with the sintering additive content of 12 wt% revealed a fracture toughness of over 10 MPa m1/2 after 60 min of BN interface deposition, which is 104.31% higher than that of the composites prepared without BN coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.