Microstructure and mechanical properties of Mg–Zn–Ca alloy processed by equal channel angular pressing

Abstract

An ultrafine-grained (UFG) Mg–5.12 wt.% Zn–0.32 wt.% Ca alloy with an average grain size of 0.7 μm was produced by subjecting the as-extruded alloy to equal channel angular pressing (ECAP) for 4 passes at 250 °C. The fine secondary phase restricted the dynamic recrystallized (DRXed) grain growth during the ECAP processing, resulting in a remarkable grain refinement. A new texture was formed in the ECAPed Mg alloy with the {0 0 0 2} plane inclined at an angle of 58° relative to the extrusion direction. The yield stress (YS) was decreased in the as-ECAPed alloy with finer grains, indicating that the texture softening effect was dominant over the strengthening from grain refinement. The ductility of the as-ECAPed alloy was increased to 18.2%. The grain refinement caused an obvious decrease in work hardening rate in the as-ECAPed alloy during tensile deformation at room temperature.