Abstract
The aims of this study are to investigate the effect of Y (yttrium) addition in the Mg-Al- Ca alloys on microstructure and mechanical properties. In additions, the alloys were solution treated in order to achieve a better understanding of the precipitation mechanisms. The as-cast microstructure of Mg-5Al-3Ca alloy and Mg-5Al-3Ca-xY alloys contains dendritic α-Mg matrix and eutectic intermetallic compound at grain boundary. The hardness values of Mg-Al-Ca alloy with Y additions were slightly increased than that of Mg-Al-Ca with no Y addition. It is because of reduction of α-Mg phase and presence of (Mg,Al)2Ca and Al-Y rich intermetallic phase at grain boundary and α-Mg matrix grains. Also, hardness value of yttrium (Y) containing alloys was increased with increasing Y contents. Compared to Mg-5Al-3Ca alloy, maximum strength and yield strength of the alloys with Y additions have slightly increased with increasing Y additions in the case of as-cast samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.