Abstract
In order to join the similar magnesium alloy, a novel Zn-Mg-Al filler metal was designed and applied to braze AZ31B plates by using high-frequency induction brazing technique. The microstructure, phase constitution and fracture morphology of the brazed joint were investigated. The experimental results show that MgZn2 phase in the original filler metal is completely consumed in the brazing process. Moreover, α-Mg solid solution and α-Mg+MgZn eutectoid structure formed in the brazing region due to the intensive alloying between the molten filler metal and the base metal in the brazing process. Test results indicate that the shear strength of the brazed joint is 56 MPa. The fracture morphology of the brazed joint shows intergranular fracture mode, where crack originates from the hard α-Mg+MgZn eutectoid structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.