Abstract
In situ TiB and TiC particle-reinforced titanium matrix composites (TMCs) based on a near-β Ti-5Al-5Mo-5V-3Cr alloy (Ti-5553) reacting chemically with B4C were processed by spark plasma sintering (SPS). The influence of powder milling parameters (low-energy mixing or high-energy milling) on the chemical reaction behavior between the matrix and the B4C particles during sintering was investigated. Taking the microstructure into account, characterization of the particle strengthening effect was carried out under compressive loading conditions. High-energy milling resulted in a significantly higher degree of B4C conversion during sintering. This was attributed to plastic deformation of the initial matrix powder and more homogeneous distribution of the B4C particles accompanied by a significant reduction in cluster formation. In comparison to the unreinforced Ti-5553 matrix, the hardness, stiffness, and compressive strength of the TMCs were successfully increased due to particle reinforcement. The powder milling treatment improved these properties further—a phenomenon directly associated with the higher degree of B4C conversion. Instead of the expected formation of stoichiometric TiC, the formation of nonstoichiometric TiC1−x with x ≈ 0.5 was observed. Molybdenum, vanadium, and chromium formed a solid solution in TiB and TiC1−x. Additionally, the titanium content in the matrix particles was markedly reduced, while the aluminum content roughly doubled.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.