Abstract
The influence of Cr3C2 and VC addition on the microstructure and mechanical properties of WC–MgO composites hot-pressed at 1650°C for 90min was comprehensively investigated. The grain growth of WC was significantly retarded and the homogeneity of MgO particulate dispersion was effectively improved with the addition of 0.5wt.% Cr3C2 or 0.5wt.% VC. The indentation size effect (ISE) on hardness was restrained and the load-independent hardness was increased by doping grain growth inhibitors. Improvements on fracture toughness of hot-pressed samples were also observed due to the refined WC grains and uniformly dispersed MgO particulates. In addition, experimental results demonstrated that Niihara's equation was preferable for estimating the indentation fracture toughness, by comparing the fracture toughness evaluated using the single-edge V-notch beam (SEVNB) method with the values estimated through the Vickers indentation technique.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Refractory Metals and Hard Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.