Abstract
Abstract Al 2 O 3 /SiC micro/nano composites containing different volume fractions (5, 10, 15, and 20 vol.%) of SiC were prepared by mixing a sub-micron alumina powder with respective amounts of either micro- or nano-sized silicon carbide powders. The powder mixtures were hot pressed 1 h at 1740 °C and 30 MPa in the atmosphere of Ar. The effect of SiC addition on the microstructure and mechanical properties, i.e. hardness, fracture toughness, and room temperature flexural strength were investigated. The flexural strength increased with increasing volume fraction of silicon carbide particles. The maximum flexural strength (655 ± 90 MPa) was achieved for the composite containing 20 vol.% of coarse-grained SiC, which is more than twice as high as in the Al 2 O 3 reference. Hardness and fracture toughness were also moderately improved. The observed improvement of mechanical properties is mainly attributed to alumina matrix grain refinement and grain boundary reinforcement.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.