Abstract
Laboratory hot rolling experiments on a low-carbon TRIP steel containing vanadium have been carried out to study the microstructure characteristics and mechanical properties. The results showed that the multiphase microstructure with ferrite, granular bainite and retained austenite could be obtained if the finish rolling initial temperature was properly decreased and the finishing temperature was controlled in the range of Ae3~ Ar3, and the tensile strength achieved 930 MPa or above. The average ferrite grain size was about 4.5 μm in this experiment, the vanadium nitrides and vanadium carbides precipitated dispersedly within ferritic grains or at grain boundaries, and the higher dislocation density existed in ferrite matrix. EBSD analyses revealed that the high angle boundaries accounted for a large proportion and the misorientation angles were within the interval between 29° and 60° mostly. When the finishing temperature was 800°C and the final air cooling temperature was 630°C, the steel had excellent mechanical properties, which was characterized by combination of high strength(about 930MPa), high elongation(21.7%), low yield/strength ratio(0.49) and as well as high work-hardening exponent(0.23).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.