Abstract
Cu matrix composites reinforced by TiB2/TiN ceramic reinforcements (Cu/TBN composites) were prepared by hot pressing method. Prior to the hot pressing, Cu/TiB2/TiN composite powders (CTBN powders), which were used as the starting materials of Cu/TBN composites, were fabricated by self-propagating high-temperature synthesis method. The CTBN particles were found to be in a special core–shell structure with a Cu–Ti alloy core and a TiB2/TiN ceramic shell. The test results presented obvious improvements in mechanical properties. The highest ultimate tensile strength reached up to 297 MPa, 77 MPa higher than that of Cu. And the highest hardness reached up to 70.7 HRF, 15.7 HRF higher than that of Cu. A comparative study indicated that the core–shell structured particles could bring about more obvious strengthening effect than the traditional irregularly shaped particles, which was due to the improved Cu/ceramics interfacial bonding, the linkage strengthening effect of both TiB2 and TiN, and higher load bearing ability of the core–shell structured reinforcements.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.