Abstract
In this study, the characteristics of commercially pure titanium (hereinafter referred as CP-Ti)/Steel joints, brazed with Zr-Ti-Ni amorphous filler metal were analyzed. The effects of brazing temperature and time on the microstructure and joining strength of the CP-Ti/Steel joints were investigated. It was observed that Ti diffused into stainless steel substrate formed a brittle reaction zone, which contained intermetallic compounds, such as τ (Ti5Cr7Fe17), (Fe, -Ni)Ti, and FeTi, observed at the joint interface. As the brazing temperature and time increased, the width of the reaction layer in the joint was observed to increase. To suppress the oxidation of the substrates, the experiment was conducted at a cooling and heating speed of 100 °C/min, under a vacuum of 5×10-5 torr. The joining strength was observed to be significantly affected by the brazing conditions, such as temperature and duration time. The shear strength test showed that the strength increased for 15 min and then sharply decreased. This was attributed to the formation of brittle intermetallic compounds, like (Fe, Ni)Ti. The joint brazed at 880 °C for 15 min showed the maximum joining strength, of 216 MPa.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.