Microstructure and mechanical properties of austempered AISI 9255 high-silicon steel

Abstract

ABSTRACTThe present investigation is focused on evaluating the microstructure and mechanical properties of American Iron and Steel Institute 9255 high-silicon steel austempered at different temperatures and durations. Material characterisation was done using a scanning electron microscope and an X-ray diffractometer. Results show the bainite microstructure over a temperature range of 280–400°C. Bainite structure gains coarseness at higher temperatures at 360 and 400°C. A significant improvement in the tensile properties was observed for all austempered specimens; with a maximum tensile strength of 1852 MPa and elongation up to 35%. An excellent strain hardening response was observed from the samples austempered at temperatures of 360 and 400°C. Tensile properties were found to be superior at 15 min of austempering duration for all austempering temperatures.