Abstract
Al-Mg-Si (AA6xxx) series alloys have been used widely in automotive industry for lightweight purpose. This work focuses on developing a short process for manufacturing Al-0.5Mg-1.3Si (wt.%) alloy sheets with good mechanical properties. Hereinto, a preparation route without homogenization was proposed on the basis of sub-rapid solidification (SRS) technique. The sample under SRS has fine microstructure and higher average partition coefficients of solute atoms, leading to weaker microsegregation owing to the higher cooling rate (160 °C/s) than conventional solidification (CS, 30 °C/s). Besides, Mg atoms tend to be trapped in Al matrix under SRS, inducing suppression of Mg2Si, and promoting generation of AlFeSi phase. After being solution heat treated (T4 state), samples following the SRS route have lower yield strength compared with that by CS route, indicating better formability in SRS sample. After undergoing pre-strain and artificial aging (T6 state), the SRS samples have comparable yield strength to CS samples, satisfying the service requirements. This work provides technological support to industrially manufacture high performance AA6xxx series alloys with competitive advantage by a novel, short and low-cost process, and open a door for the further development of twin-roll casting based on SRS technique in industries.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.