Abstract
AbstractComposites of Al2O3/ZrO2 (containing 25, 50, and 75 vol% ZrO2) were prepared by mixing Al2O3 and ZrO2 suspensions. The microstructural control via two‐step sintering (TSS) was the main objective of this work. For this purpose, different sintering curves were constructed, aiming to achieve the best temperature combination for the sintering steps that provides higher density and finer microstructure. The results were compared with single‐step sintering (SSS). Furthermore, microhardness and fracture toughness were measured for the best TSS specimens under each composition. The results showed that the high densities were obtained, and the reduction of grain size was greater than 40% for two‐step sintered specimens, compared to SSS ones. Consequently, microhardness values increased. However, fracture toughness values remained unchanged.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Applied Ceramic Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.