Abstract
AbstractAn elemental powder mixture of composition Ti–35 wt-%Al was cold extruded, reactive hot isostatic pressed at 1000°C, and subsequently annealed at 1250°C. A duplex microstructure was formed having elongated lamellar regions of Ti3Al/TiAl within a TiAl matrix. Specimens were tested in compression at temperatures between room temperature and 900°C. The material exhibits good deformability at 700°C and above. In this region, the typical stress–strain behaviour accompanying dynamic recrystallisation is observed. Matrix and lamellar regions both undergo deformation. Below 700°C, pseudoplasticity occurs, which is related to homogeneous formation of microcracks. The observed behaviour is compared with that of a cast material of similar composition.MST/1545
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.