Abstract
For the development of advanced nanoscale multilayer protective coatings, proper design of microstructure and chemical composition of carbon containing sequential transition metal nitride nanolayers is an important issue. In this work, five different nanostructured CrCN/ZrCN multilayer coatings were deposited periodically by cathodic arc evaporation. The bilayer period of the CrCN/ZrCN multilayer coatings was kept at 20 nm. The C2H2 gas flow ratio was adjusted from 6.3 to 20.0% for achieving CrCN/ZrCN multilayer coatings with 2.3–4.2 at.% carbon content. Nanolaminated CrCN and ZrCN nitride layers and thin amorphous carbon nitride mixed nanolayers ∼5 nm thick were obtained as the carbon content reached 4.2 at.%. It was found that the hardness and adhesion quality were strongly improved by the carbon addition to the CrCN/ZrCN multilayer coatings. An increase of 2.6–4.6 GPa in hardness was found for the CrCN/ZrCN multilayer coatings due to the balance of solution hardening effect of carbon atoms and the softening by the amorphous mixed nanolayer. An optimal combination of high hardness, 28.9 GPa, and good adhesion, 41 N of upper critical load were achieved when the carbon content was 4.2 at.% for the CrCN/ZrCN multilayer coatings.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.