Abstract
In the present investigation, we provide results on the casting, homogenization, and deformation behavior of a new Al-containing refractory high-entropy alloy, namely the equiatomic Nb-Mo-Cr-Ti-Al. The alloy shows a dendritic microstructure after arc melting. The dendrites completely dissolve due to a heat treatment at 1300 °C for 20 h. Besides a major phase in the form of a solid solution of W prototype structure, identified by X-ray diffraction (XRD) measurements as well as electron backscatter diffraction (EBSD), additional phases of small volume fraction within the grains and at the grain boundaries were observed. Quasistatic compression tests, performed between room temperature and 1200 °C, reveal sustaining and high yield strength up to 800 °C and an increasing ductility with increasing test temperature. The dominant deformation mechanism for quasistatic compression loading between 800 °C and 1200 °C is the 〈111〉 pencil glide of dislocations within the solid solution which was proven by the according fiber texture components, evolving during deformation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.