Abstract
Purpose This paper aims to focus on the reliability of Sn15Bi–xAg and Sn15Bi–xCu solder joints during isothermal aging. Design/methodology/approach The effects of Ag or Cu additions on the microstructure, interfacial metallic compound layer and shear strength of Sn–15Bi (Sn15Bi) based solder joints during were investigated. The effects of Ag or Cu additions on the microstructure and tensile properties of Sn15Bi-based bulk solders were also investigated to provide a comprehensive analysis. The interfacial morphology and microstructure were observed by scanning electron microscopy and the composition in the structure was examined by energy dispersive spectrometer. The shear tests were carried out on the as-soldered and as-aged joints using a ball shear tester. Findings The results revealed that by adding Ag or Cu, the microstructure of Sn15Bi solder can be refined. Ag addition increased the tensile strength of Sn15Bi solder but had little effect on elongation. However, Cu addition decreased the tensile strength and elongation of Sn15Bi solder. For solder joints, Ag addition increased the shear strength and toughness of Sn15Bi/Cu joints but Cu addition decreased the shear strength and toughness of Sn15Bi/Cu joints. Originality/value The authors can potentially provide a replacement for Sn40Pb traditional solder with Sn15Bi solder by alloying Ag or Cu due to its lower cost and similar melting point as Sn–Pb solder.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.