Abstract
The oriented Fe83Ga17 alloy rods with various NbC contents less than 1at% were prepared by the directional solidification method at a growth rate of 720 mmh−1. Low NbC-content was found to affect the oriented grain growth and slightly improve the orientation. Flat grain boundaries in the alloys with low NbC contents less than 0.2at% became greatly curved at higher NbC contents, and a large amount of Nb-rich precipitates were observed in the alloys with high NbC contents. Small amounts of NbC, less than 0.2at%, resulted in an increase in magnetostrictive strain due to the improvement of the orientation, and a high magnetostrictive strain value of 335 10−6 under a pre-stress of 15 MPa was obtained in the 0.1at% NbC-doped alloys. The magnetostrictive performance obviously decreased with the NbC addition higher than 0.5at%, and the strain sensitivity under no pre-stress was lower than that in the binary Fe-Ga alloy.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Minerals, Metallurgy, and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.