Abstract
The microstructure and magnetic viscosity of bulk amorphous Nd60Fe20Al5Co10B5,prepared by suction casting the molten alloy into a copper mold under an argon atmosphere, have been investigated. The results show that clusters with size 3–5 nm are found to be embedded in the amorphous matrix of as-cast bulk amorphous Nd60Fe20Al5Co10B5 alloy. The Nd60Fe20Al5Co10B5 alloy shows hard magnetic behavior at room temperature, with an intrinsic coercivity of 360 kA/m and a remanence of 69.39 mT. The magnetic viscosity of bulk amorphous Nd60Fe20Al5Co10B5 has been investigated on the major hysteresis loop, and simple logarithmic time dependence is observed. A value for the fluctuation field of 8.24 kA/m is obtained. Analysis based on a Henkel plot is used to confirm the existence of magnetic interaction among clusters. The coercivity mechanism responsible for the hard magnetic behavior of bulk amorphous Nd60Fe20Al5Co10B5 alloy is also discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.