Abstract
Bulk isotropic and anisotropic Nd13.5Fe80.4Ga0.5B5.6 and Nd13.5Fe80.4Ga0.5B5.6/Fe magnets were synthesized by applying spark plasma sintering (SPS) technique. The effect of hot-pressing temperature on the magnetic properties of hot-pressed (HP) and hot-deformed (HD) magnets without additive and with 5% Fe addition was investigated. With increasing sintering temperature for HP magnets, the grain grew gradually. For HD magnets, the optimal magnetic properties could be obtained at hot-pressing temperature 680°C due to the development of desired c-axis texture and uniform microstructure, which resulted from the appropriate and uniform grain size in HP magnets. Fe addition could enhance remanence (Br) and magnetic energy products ((BH)m) of HP and HD magnets. However, the maximum magnetic energy product of HD magnets decreased when hot-pressing temperature was higher than 650°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callSimilar Papers
More From: Materials Science Forum
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.