Abstract
Multifunctional nanocomposites consisting of at least one ferromagnetic phase (e.g. FeCo) and one protective, wear resistant phase (e.g. TiN) are of interest for applications as sensors or actuators in harsh environments. This paper reports on the fabrication and characterization of nanocomposite thin films, prepared from FeCo/Ti metallic precursor multilayer composition spreads using a combinatorial sputter-deposition system. After deposition, the composition spread was annealed in nitrogen (5 × 10 5 Pa pressure) at 850 °C for 1.5 h, leading to preferential nitriding of Ti to TiN, thus forming the protective phase. Automated energy dispersive X-ray analysis, Auger electron spectroscopy, X-ray diffraction measurements, transmission electron microscopy (TEM) and vibrating sample magnetometry were used for the characterization of the as deposited and nitrided composition spreads. As an unexpected result, the appearance of a Heusler phase (Co 2FeSi) in the nanocomposite was observed by TEM. After N 2 annealing, the nanocomposites show reduced saturation magnetization values μ 0M S between 0.5 and 0.95 T and improved coercive field values μ 0H c between 4 and 13.8 mT, dependent on the TiN content.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.