Al 18B 4O 33w/Co composite particles were prepared successfully through electroless plating Co on Al 18B 4O 33 whiskers. The growth behavior of the coatings, the effect of the process parameters and the electromagnetic properties of the prepared Al 18B 4O 33w/Co composite particles were investigated. The reduced Co nucleated first on the pre-activated surface of the whiskers to form insular particles which then grew larger gradually and eventually merged together to form continuous coatings. The reaction rate increased but the mass gain decreased with the increase of the bath pH and the bath temperature. The crystallinity of the deposited Co decreased with the increase of phosphorous content as well as the bath temperature. The effect of loading is much weaker compare to that of bath pH and bath temperature. The permittivity and the permeability of the prepared Al 18B 4O 33w/Co composite particles are markedly higher than those of the raw Al 18B 4O 33 whiskers in microwave band. Relaxation resonance is found in the samples with thick Co coatings due to the presence of eddy current, which deteriorates the permeability of the Al 18B 4O 33w/Co composite particles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.