Abstract
Cesium tungsten oxides (Cs x WO 3) were synthesized by solvothermal reactions using ethanol and 57.1 vol% ethanol aqueous solution at 200 °C for 12 h, and the effects of post annealing in ammonia atmosphere on the microstructure and electrical–optical properties were investigated. Agglomerated particles consisting of disk-like nanoparticles and nanorods of Cs x WO 3 were formed in the pure ethanol and ethanol aqueous solutions, respectively. The samples retained the original morphology and crystallinity after annealing in ammonia atmosphere up to 500 °C, while a small amount of nitrogen ion were incorporated in the lattice. The as-prepared Cs x WO 3 sample showed excellent near infrared (NIR) light shielding ability as well as high transparency in the visible light region. The electrical resistivity of the pressed pellets of the powders prepared in pure ethanol and 57.1 vol% ethanol aqueous solution greatly decreased after ammonia annealing at 500 °C, i.e., from 734 to 31.5 and 231 to 3.58 Ω cm, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.