Abstract
Bulk Al-8Fe-2Mo-2V-1Zr (wt.%) alloys were produced by melt spinning which can give rise to develope a nano crystalline structure in terms of rapid cooling and subsequent hot extrusion. The bulk alloys exhibited multi-phase microstructures consisting of ultra fine equiaxed grains with the average grain size of 100nm and a fine intermetallic Al-Fe, Al-V and Al-Zr based phase having less than 50nm in particle size. From compression test, it was revealed that the bulk alloys have very high yield strength at both room temperature (942MPa) and elevated temperatures (651MPa at 473K, 500MPa at 573K, respectively).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.