Abstract
The microstructure and aging behavior of Cu-1.8wt%Be-0.2wt%Co alloy specimens processed by high-pressure torsion (HPT) at room temperature (RT) and 150°C after solution treatment have been studied. Application of HPT processing at RT and 150°C under an applied pressure of 5 GPa for 10 revolutions at 1 rpm to alloy specimens (RT-and 150°C-specimen) produces an ultra-fine grained structure with a grain size of 70 nm. The hardnesses of the RT-and 150°C-specimens increase with equivalent strain up to 7 and then saturate at constant values of 400 and 430 Hv, respectively. Annealing the RT-specimen at 150°C for 10 min increases the hardness from 400 to 430 Hv. Transmission electron microscopy observations of the 150°C-specimen and the RT-specimen annealed at 150°C reveal that there are no intragranular and intergranular precipitates. It is suggested that the higher hardness of the 150°C-specimen than the RT-specimen is ascribed to the segregation of Be atoms on dislocations during HPT processing at 150°C. The RT-and 150°C-specimens harden rapidly and exhibit maximum values of hardness at 3 min during aging at 320°C. The increase in the hardness is attributed to the precipitation of finely dispersed G.P. zones.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have