Abstract
Semi-solid AZ91 magnesium alloys were produced using a cooling plate followed by quenching in the mold. The cast and T6 heat treated microstructures were microscopically characterized and subjected to hardness tests. It was found that the resultant microstructure in water quenched semi-solid specimen were finer than that in conventional permanent mold cast specimen. The hardness tests also showed that the hardness of quenched semi-solid cast specimen was higher than that of permanent mold cast specimen. This was attributed to large amount of precipitates which results from fine precipitation of eutectic phase at intergranular areas during the aging treatment after its complete dissolution.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.