Microstructure analyses and phase-field simulation of partially divorced eutectic solidification in hypoeutectic Mg-Al Alloys

Abstract

In this study the partially divorced eutectic microstructure of α-Mg and β-Mg 17 Al 12 was investigated by electron backscatter diffraction, transmission electron microscopy, and phase-field modeling in hypoeutectic Mg-Al alloys. The orientation relationships between the individual eutectic α grains, eutectic β phase, and primary α grains were investigated. While the amount of eutectic morphology is primarily determined by the Al content, the in-depth microstructure analyses and the phase-field simulation suggest non-interactive nucleation and growth of eutectic α phase in the β phase grown on the interdendritic primary α dendrites. Also, phase-field simulations showed a preferred nucleation sequence where the β phase nucleates first and subsequently triggers the nucleation of eutectic α phase at the moving β phase solidification front, which supports the microstructural analysis results.